Análise da resistência à compressão axial do concreto, com cinza da casca do café
| dc.contributor.advisor | Mestre Thiago Pastre Pereira | |
| dc.contributor.author | Nunes, Derlon Silva | |
| dc.date.accessioned | 2023-07-11T19:14:47Z | |
| dc.date.available | 2023-07-11T19:14:47Z | |
| dc.date.issued | 2020-12-17 | |
| dc.description.abstract | A busca por métodos alternativos na construção civil, que visa a diminuição do consumo de materiais finitos e menos impactos negativos ao meio ambiente, está cada vez mais presentes nas atividades de campo e, a cada dia, várias pesquisas são desenvolvidas com esse intuito. A fim de contribuir para uma economia sustentável e que gere menos impactos ambientas, este trabalho propõe a determinação de um traço através de pesquisa laboratorial, a partir do concreto, substituindo parte do cimento (em massa) por cinzas da casca de café queimado. Várias pesquisas com outros materiais alternativos como cinza da casca de arroz, borracha de pneu e resíduo de construção e demolição, trouxeram resultados satisfatórios no desempenho físico do concreto. A partir desse conceito, foi determinado um traço de referência para o concreto; no entanto, devido à dificuldade em obter a cinza da casca de café, foi realizada a confecção de corpos de prova de argamassa (dos quais foi extraído o agregado graúdo do traço adotado para obter a “argamassa”) para verificar a melhor porcentagem de resíduo a ser utilizada na confecção dos corpos de provas de concreto, evitando, assim, desperdícios de materiais. A partir dos resultados obtidos no ensaio de compressão axial da argamassa, observou-se que com 5 % de substituição do cimento por cinza, houve uma diminuição considerável na resistência axial. Com isso, foi determinado que, no concreto, seria analisada a utilização de 2 % e 5 % de cinza em relação ao cimento. No entanto, através dos ensaios de compressão axial e diametral, foi possível observar que as cinzas não apresentaram nenhuma melhora na resistência do concreto, portanto, não apresentando o mesmo comportamento da cinza da casca de arroz no concreto. Ao que tudo indica pelos resultados obtidos neste trabalho, a cinza teve influência tal como os vazios, assim, diminuindo a resistência de forma significativa. | |
| dc.description.abstract1 | The search for alternative methods in civil construction, that aims the decrease in consumption of finite materials and less negative impacts to the environment is increasingly present in field activities and, everyday, several researches are developed for this purpose. In order to contribute to a sustainable economy, that generates less environmental impact, this work proposes the determination of a trait, through laboratory reseach, from concrete, replacing part of the cement (in mass) with burnt coffee husk. A lot of researches with other alternative materials, like ashes made from rice husk, tire rubber and residue obtained from construction and demolition brought satisfactory results to the physical performance of concrete. Based on this concept, a reference trait was determined for the concrete; however, due to the difficulty to obtain the coffee husk ashes, mortar specimens were made (from which it was extracted the coarse aggregate of the adopted trait to obtain the “mortar”) to verify the best percentage of residue to be used in making concrete specimens, thus avoiding waste of materials. From the results obtained in the mortar axial compression test, it was observed that, with a 5 % replacement from cement to ashes, there was a considerable decrease in the axial endurance. Therewith, it was determined that, it would be analyzed 2 % and 5 % replacements of ashes with respect to cement. However, through axial compression and diametral tests, it was possible to notice that the ashes showed no improvement in the strength of the concrete, therefore, not showing the same behavior as rice husk ashes in the concrete. Based in the results obtained in this work, it seems that the ash had influence such as the voids, thus, decreasing the endurance significantly. | |
| dc.identifier.uri | http://hdl.handle.net/20.500.14387/1065 | |
| dc.language.iso | Português | |
| dc.publisher.campi | Piumhi | |
| dc.publisher.country | Brasil | |
| dc.publisher.institution | Instituto Federal de Minas Gerais - Campus Avançado Piumhi | |
| dc.publisher.program | Graduação Bacharelado em Engenharia Civil | |
| dc.rights | Acesso aberto | |
| dc.subject.keyword | Concreto - materiais alternativos | |
| dc.subject.keyword | Concreto - resíduo de café | |
| dc.subject.keyword | Concreto - produção e ensaios | |
| dc.subject.keyword | Engenharia civil | |
| dc.title | Análise da resistência à compressão axial do concreto, com cinza da casca do café | |
| dc.type | Trabalho de Conclusão de Curso |