AVALIAÇÃO DAS PROPRIEDADES MECÂNICAS E METALÚRGICAS DO AÇO 4130H SOB DIFERENTES CONDIÇÕES DE TRATAMENTO TÉRMICO

Página do item simplificado
dc.contributor.advisorDr. Gabriel Mendes de Almeida Carvalho
dc.contributor.authorJoice Paloma Faria
dc.contributor.coadvisorPedro Henrique Degasperi Escolástico
dc.date.accessioned2025-06-23T11:44:47Z
dc.date.available2025-06-23T11:44:47Z
dc.date.issued2025-05-06
dc.description.abstractO trabalho analisou o tratamento térmico mais adequado entre têmpera com resfriamento ao ar e têmpera com resfriamento em água, utilizando métodos experimentais, tendo como material base o aço 4130H. A pesquisa foi conduzida por meio da realização de ensaios mecânicos de dureza e ensaios metalográficos, a fim de avaliar as mudanças microestruturais e as propriedades mecânicas resultantes de cada tratamento térmico. A dureza foi mensurada utilizando o método Rockwell C, enquanto a análise metalográfica permitiu a observação das transformações de fase ocorridas nas amostras tratadas. Os resultados mostraram que a têmpera com resfriamento em água proporciona um aumento significativo da dureza devido à formação de martensita, porém com maior risco de tensões residuais e trincas. Por outro lado, a têmpera com resfriamento ao ar resultou em uma dureza moderada, mas com uma microestrutura mais homogênea e menor suscetibilidade a defeitos. Com base na análise comparativa das propriedades mecânicas, conclui-se que a escolha do tratamento térmico deve considerar o uso final da peça: para aplicações que exigem máxima dureza e resistência ao desgaste, a têmpera em água é recomendada.
dc.description.abstract1The study analyzed the most suitable heat treatment between air cooling quen- ching and water cooling quenching, using experimental methods to support the choice, with 4130H steel as the base material. The research was conducted through mecha- nical hardness tests and metallographic analysis to evaluate the microstructural changes and mechanical properties resulting from each heat treatment. Hardness was measured using the Rockwell method, while metallographic analysis allowed for the observation of phase transformations in the treated samples. The results showed that water quenching significantly increases hardness due to the formation of martensite, but with a higher risk of residual stresses and cracking. On the other hand, air quenching resulted in moderate hardness, but with a more homogeneous microstructure and lower susceptibility to defects. Based on the comparative analysis of the mechanical properties, it is concluded that the choice of heat treatment should consider the final application of the part: for applications requiring maximum hardness and wear resistance, water quenching is recommended.
dc.identifier.urihttp://hdl.handle.net/20.500.14387/2330
dc.language.isoPortuguês
dc.publisher.campiBetim
dc.publisher.countryBrasil
dc.publisher.institutionInstituto Federal de Mias Gerais - Campus Betim
dc.rightsAcesso aberto
dc.subject.keywordTêmpera; 4130H; Dureza HRC; Microestrutura.
dc.titleAVALIAÇÃO DAS PROPRIEDADES MECÂNICAS E METALÚRGICAS DO AÇO 4130H SOB DIFERENTES CONDIÇÕES DE TRATAMENTO TÉRMICO
dc.typeTrabalho de Conclusão de Curso
Arquivos
Pacote Original
Agora exibindo 1 - 1 de 1
Imagem de Miniatura
Nome:
TCC_JOICE PALOMA FARIA.pdf
Tamanho:
114.58 MB
Formato:
Adobe Portable Document Format
Descrição:
Baixar
Licença do Pacote
Agora exibindo 1 - 1 de 1
Imagem de Miniatura
Nome:
license.txt
Tamanho:
1.79 KB
Formato:
Item-specific license agreed to upon submission
Descrição:
Baixar
Coleções
Trabalho de Conclusão de Curso